- - Carbon   Carbon  Carbon  Carbon  Carbon  Carbon  Carbon  Carbon     
- - /Epoxy   /Epoxy  Carbon  /Epoxy  /Epoxy  /Epoxy  /Peek   /Polyimide 
- - AS4      AS4     T300    T800    IM7     IM7     AS4     Avimid     
Property  Symbol  /3501-6  3501-6[24] /914-C[24]  /3900-2  /8551 -7 /8552  /APC2  /K-III 
 Density [g/cc]  $\rho$                           1.58           1.6 -      
 Longitudinal Modulus [GPa]  $E_1$                142           138 110
 Transverse Modulus [GPa]  $E_2$                  10.3           10.2 8.3
 In-plane Shear Modulus [GPa]  $G_{12}$           7.2           5.7 5.7
 In-plane Poisson's Ratio  $\nu_{12}$             0.27           0.3 -      
 Transverse Shear Modulus [GPa]  $G_{23}$         3.93           -       -      
 Longitudinal Tensile Strength [MPa]  $F_{1t}$    1830           2070 -      
 Transverse Tensile Strength [MPa]  $F_{2t}$      57           86 37
 Longit. Compressive Strength [MPa]  $F_{1c}$     1096           1360 1000
 Transv. Compressive Strength [MPa]  $F_{2c}$     228           -       -      
 In-plane Shear Strength [MPa]  $F_6$             71           186 63
 Interlaminar Shear Strength [MPa]  $F_4$         -                 150 -      
 Ult. Longit. Tens. Strain [\%] $\epsilon_{1t}$   1.29           1.45 -      
 Ult. Transv. Tens. Strain [\%] $\epsilon_{2t}$   0.436           -       -      
 Ult. Longit. Comp. Strain [\%] $\epsilon_{1c}$   1.175           -       -      
 Ult. Transv. Comp. Strain [\%] $\epsilon_{2c}$   2           -       -      
 Ultimate Shear Strain [\%]  $\gamma_{6u}$        2           -       -      
Intra-lam frac. tough. I [$J/m^2$] $G_{Ic}$   220           -       -      
Intra-lam frac. tough. II [$J/m^2$] $G_{IIc}$ -                 -       -      
 Longitudinal CTE [$10^{-6}/^\circ C$]  $\alpha_1$ -0.9           0.5 -      
 Transverse CTE [$10^{-6}/^\circ C$]  $\alpha_2$   27           30 -      
 Stress-free temperature [$^\circ C$]  $SFT$       177           -       -      
 Longitudinal moisture expansion  $\beta_1$       0           -       -      
 Transverse moisture expansion  $\beta_2$         0.2           -       -      
 Fiber Volume Fraction   $V_f$                    0.6           0.61 -      
 Void Content    $V_v$                            -                 -       0.005
 Fiber Misalignment [deg]  $\alpha_\sigma$        1.7           2.74 1.52
 Ply thickness [mm]  $t_k$                        0.125           0.125 0.125