- - E-Glass    S-Glass    E-Glass   Kevlar49   E-Glass   E-Glass
- - /Epoxy    /Epoxy    /Isophtalic   /Epoxy  /Epoxy  /Epoxy
Property  Symbol             Polyester    LY556 [24] MY750 [24]
 Density [g/cc]  $\rho$ 2.076   1.85 1.38    
 Longitudinal Modulus [GPa]  $E_1$ 45   37.9 75.8    
 Transverse Modulus [GPa]  $E_2$ 12   11.3 5.5    
 In-plane Shear Modulus [GPa]  $G_{12}$ 5.5   3.3 2.07    
 In-plane Poisson's Ratio  $\nu_{12}$ 0.19   0.3 0.34    
 Transverse Shear Modulus [GPa]  $G_{23}$ 4.57     -   -       
 Longitudinal Tensile Strength [MPa]  $F_{1t}$ 1020   903 1380    
 Transverse Tensile Strength [MPa]  $F_{2t}$ 40   40 34.5    
 Longit. Compressive Strength [MPa]  $F_{1c}$ 620   357 586    
 Transv. Compressive Strength [MPa]  $F_{2c}$ 140   68 138    
 In-plane Shear Strength [MPa]  $F_6$ 60   40 44.1    
 Interlaminar Shear Strength [MPa]  $F_4$   -      -  150    
 Ult. Longit. Tensile Strain [\%]  $\epsilon_{1t}$ 1.29   1.64 1.45    
 Ult. Transv. Tensile Strain [\%]  $\epsilon_{2t}$ -          -       -          
 Ult. Longit. Comp. Strain [\%]    $\epsilon_{1c}$ -          -       -          
 Ult. Transv. Comp. Strain [\%]    $\epsilon_{2c}$ -          -       -          
 Ultimate Shear Strain [\%]        $\gamma_{6u}$    -          -       -          
Intra-lam frac. tough. I [$J/m^2$] $G_{Ic}$  158   167 256    
Intra-lam frac. tough. II [$J/m^2$] $G_{IIc}$ 308   228 443    
 Longitudinal CTE [$10^{-6}/^\circ C$]  $\alpha_1$ 3.7   6.5 -2    
 Transverse CTE [$10^{-6}/^\circ C$]  $\alpha_2$ 30   22 60    
 Stress-free temperature [$^\circ C$]  $SFT$ 126     -  126    
 Longitudinal moisture expansion  $\beta_1$ 0   0 0.01    
 Transverse moisture expansion  $\beta_2$ 0.2   0.2 0.2    
 Fiber Volume Fraction          $V_f$    0.6   0.5 0.6    
 Void Content                    $V_v$   0.02 -                                    
 Fiber Misalignment [deg]  $\alpha_\sigma$ 2.97   3.53 1.34    
 Ply thickness [mm]  $t_k$ 0.144   0.144 0.144